Grade CU5MCuC Nickel vs. SAE-AISI 1064 Steel
Grade CU5MCuC nickel belongs to the nickel alloys classification, while SAE-AISI 1064 steel belongs to the iron alloys. They have a modest 31% of their average alloy composition in common, which, by itself, doesn't mean much. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is grade CU5MCuC nickel and the bottom bar is SAE-AISI 1064 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 22 | |
| 12 to 13 |
| Fatigue Strength, MPa | 170 | |
| 300 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 720 to 730 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 470 to 480 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 400 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1370 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 45 | |
| 1.8 |
| Density, g/cm3 | 8.2 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 7.7 | |
| 1.4 |
| Embodied Energy, MJ/kg | 110 | |
| 19 |
| Embodied Water, L/kg | 230 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 79 to 81 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 | |
| 600 to 630 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 20 | |
| 25 to 26 |
| Strength to Weight: Bending, points | 19 | |
| 23 |
| Thermal Shock Resistance, points | 16 | |
| 25 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0.6 to 0.7 |
| Chromium (Cr), % | 19.5 to 23.5 | |
| 0 |
| Copper (Cu), % | 1.5 to 3.5 | |
| 0 |
| Iron (Fe), % | 22.2 to 37.9 | |
| 98.4 to 98.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 2.5 to 3.5 | |
| 0 |
| Nickel (Ni), % | 38 to 44 | |
| 0 |
| Niobium (Nb), % | 0.6 to 1.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.050 |