Grade CW2M Nickel vs. EN 1.5418 Steel

Grade CW2M nickel belongs to the nickel alloys classification, while EN 1.5418 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is grade CW2M nickel and the bottom bar is EN 1.5418 steel.

Grade CW2M (J26455) Cast Nickel EN 1.5418 (37Mo2) Molybdenum Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		210
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.29
Poisson's Ratio		0.29

Shear Modulus, GPa		83
Shear Modulus, GPa		73

Tensile Strength: Ultimate (UTS), MPa		560
Tensile Strength: Ultimate (UTS), MPa		490 to 1780

Thermal Properties

Latent Heat of Fusion, J/g		330
Latent Heat of Fusion, J/g		250

Maximum Temperature: Mechanical, °C		960
Maximum Temperature: Mechanical, °C		400

Melting Completion (Liquidus), °C		1520
Melting Completion (Liquidus), °C		1460

Melting Onset (Solidus), °C		1460
Melting Onset (Solidus), °C		1420

Specific Heat Capacity, J/kg-K		430
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		12
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Base Metal Price, % relative		70
Base Metal Price, % relative		2.1

Density, g/cm³		8.8
Density, g/cm³		7.8

Embodied Carbon, kg CO₂/kg material		12
Embodied Carbon, kg CO₂/kg material		1.5

Embodied Energy, MJ/kg		170
Embodied Energy, MJ/kg		19

Embodied Water, L/kg		290
Embodied Water, L/kg		47

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		18
Strength to Weight: Axial, points		17 to 63

Strength to Weight: Bending, points		17
Strength to Weight: Bending, points		18 to 42

Thermal Shock Resistance, points		16
Thermal Shock Resistance, points		14 to 53

Alloy Composition

Carbon (C), %		0 to 0.020
Carbon (C), %		0.35 to 0.4

Chromium (Cr), %		15 to 17.5
Chromium (Cr), %		0

Copper (Cu), %		0
Copper (Cu), %		0 to 0.25

Iron (Fe), %		0 to 2.0
Iron (Fe), %		97.8 to 98.9

Manganese (Mn), %		0 to 1.0
Manganese (Mn), %		0.6 to 0.9

Molybdenum (Mo), %		15 to 17.5
Molybdenum (Mo), %		0.2 to 0.3

Nickel (Ni), %		60.1 to 70
Nickel (Ni), %		0

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0 to 0.025

Silicon (Si), %		0 to 0.8
Silicon (Si), %		0 to 0.3

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.025

Tungsten (W), %		0 to 1.0
Tungsten (W), %		0