Grade CW2M Nickel vs. EN 1.5521 Steel
Grade CW2M nickel belongs to the nickel alloys classification, while EN 1.5521 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is grade CW2M nickel and the bottom bar is EN 1.5521 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 23 | |
| 11 to 21 |
| Fatigue Strength, MPa | 190 | |
| 210 to 310 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 83 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 560 | |
| 430 to 1390 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 300 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 960 | |
| 400 |
| Melting Completion (Liquidus), °C | 1520 | |
| 1460 |
| Melting Onset (Solidus), °C | 1460 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 1.9 |
| Density, g/cm3 | 8.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 1.4 |
| Embodied Energy, MJ/kg | 170 | |
| 19 |
| Embodied Water, L/kg | 290 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 44 to 230 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 | |
| 250 to 630 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 18 | |
| 15 to 49 |
| Strength to Weight: Bending, points | 17 | |
| 16 to 35 |
| Thermal Shock Resistance, points | 16 | |
| 13 to 41 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 to 0.020 | |
| 0.16 to 0.2 |
| Chromium (Cr), % | 15 to 17.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 2.0 | |
| 98 to 98.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.9 to 1.2 |
| Molybdenum (Mo), % | 15 to 17.5 | |
| 0 |
| Nickel (Ni), % | 60.1 to 70 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.8 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |
| Tungsten (W), % | 0 to 1.0 | |
| 0 |