Grade CW2M Nickel vs. SAE-AISI H24 Steel

Grade CW2M nickel belongs to the nickel alloys classification, while SAE-AISI H24 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is grade CW2M nickel and the bottom bar is SAE-AISI H24 steel.

Grade CW2M (J26455) Cast Nickel SAE-AISI H24 (T20824) Tungsten Hot-Work Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		210
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.29
Poisson's Ratio		0.29

Shear Modulus, GPa		83
Shear Modulus, GPa		78

Tensile Strength: Ultimate (UTS), MPa		560
Tensile Strength: Ultimate (UTS), MPa		720 to 1990

Thermal Properties

Latent Heat of Fusion, J/g		330
Latent Heat of Fusion, J/g		240

Melting Completion (Liquidus), °C		1520
Melting Completion (Liquidus), °C		1750

Melting Onset (Solidus), °C		1460
Melting Onset (Solidus), °C		1700

Specific Heat Capacity, J/kg-K		430
Specific Heat Capacity, J/kg-K		420

Thermal Expansion, µm/m-K		12
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		70
Base Metal Price, % relative		37

Density, g/cm³		8.8
Density, g/cm³		9.1

Embodied Carbon, kg CO₂/kg material		12
Embodied Carbon, kg CO₂/kg material		6.1

Embodied Energy, MJ/kg		170
Embodied Energy, MJ/kg		93

Embodied Water, L/kg		290
Embodied Water, L/kg		78

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		12

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		22

Strength to Weight: Axial, points		18
Strength to Weight: Axial, points		22 to 61

Strength to Weight: Bending, points		17
Strength to Weight: Bending, points		20 to 39

Thermal Shock Resistance, points		16
Thermal Shock Resistance, points		22 to 61

Alloy Composition

Carbon (C), %		0 to 0.020
Carbon (C), %		0.42 to 0.53

Chromium (Cr), %		15 to 17.5
Chromium (Cr), %		2.5 to 3.5

Copper (Cu), %		0
Copper (Cu), %		0 to 0.25

Iron (Fe), %		0 to 2.0
Iron (Fe), %		78 to 82.4

Manganese (Mn), %		0 to 1.0
Manganese (Mn), %		0.15 to 0.4

Molybdenum (Mo), %		15 to 17.5
Molybdenum (Mo), %		0

Nickel (Ni), %		60.1 to 70
Nickel (Ni), %		0 to 0.3

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 0.8
Silicon (Si), %		0.15 to 0.4

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030

Tungsten (W), %		0 to 1.0
Tungsten (W), %		14 to 16

Vanadium (V), %		0
Vanadium (V), %		0.4 to 0.6