Grade CW2M Nickel vs. SAE-AISI H42 Steel

Grade CW2M nickel belongs to the nickel alloys classification, while SAE-AISI H42 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is grade CW2M nickel and the bottom bar is SAE-AISI H42 steel.

Grade CW2M (J26455) Cast Nickel SAE-AISI H42 (T20842) Molybdenum Hot-Work Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		210
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.29
Poisson's Ratio		0.29

Shear Modulus, GPa		83
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		560
Tensile Strength: Ultimate (UTS), MPa		700 to 1980

Thermal Properties

Latent Heat of Fusion, J/g		330
Latent Heat of Fusion, J/g		260

Melting Completion (Liquidus), °C		1520
Melting Completion (Liquidus), °C		1620

Melting Onset (Solidus), °C		1460
Melting Onset (Solidus), °C		1570

Specific Heat Capacity, J/kg-K		430
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		12
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		70
Base Metal Price, % relative		24

Density, g/cm³		8.8
Density, g/cm³		8.4

Embodied Carbon, kg CO₂/kg material		12
Embodied Carbon, kg CO₂/kg material		8.8

Embodied Energy, MJ/kg		170
Embodied Energy, MJ/kg		130

Embodied Water, L/kg		290
Embodied Water, L/kg		98

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		18
Strength to Weight: Axial, points		23 to 65

Strength to Weight: Bending, points		17
Strength to Weight: Bending, points		21 to 42

Thermal Shock Resistance, points		16
Thermal Shock Resistance, points		20 to 57

Alloy Composition

Carbon (C), %		0 to 0.020
Carbon (C), %		0.55 to 0.7

Chromium (Cr), %		15 to 17.5
Chromium (Cr), %		3.8 to 4.5

Copper (Cu), %		0
Copper (Cu), %		0 to 0.25

Iron (Fe), %		0 to 2.0
Iron (Fe), %		79.3 to 83.8

Manganese (Mn), %		0 to 1.0
Manganese (Mn), %		0.15 to 0.4

Molybdenum (Mo), %		15 to 17.5
Molybdenum (Mo), %		4.5 to 5.5

Nickel (Ni), %		60.1 to 70
Nickel (Ni), %		0 to 0.3

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 0.8
Silicon (Si), %		0

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030

Tungsten (W), %		0 to 1.0
Tungsten (W), %		5.5 to 6.8

Vanadium (V), %		0
Vanadium (V), %		1.8 to 2.2