Grade CW2M Nickel vs. R30155 Cobalt
Grade CW2M nickel belongs to the nickel alloys classification, while R30155 cobalt belongs to the iron alloys. They have 42% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is grade CW2M nickel and the bottom bar is R30155 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 210 |
| Elongation at Break, % | 23 | |
| 34 |
| Fatigue Strength, MPa | 190 | |
| 310 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 83 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 560 | |
| 850 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 960 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1520 | |
| 1470 |
| Melting Onset (Solidus), °C | 1460 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 450 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 80 |
| Density, g/cm3 | 8.8 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 9.7 |
| Embodied Energy, MJ/kg | 170 | |
| 150 |
| Embodied Water, L/kg | 290 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 230 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 | |
| 370 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 18 | |
| 28 |
| Strength to Weight: Bending, points | 17 | |
| 24 |
| Thermal Shock Resistance, points | 16 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0 to 0.020 | |
| 0.080 to 0.16 |
| Chromium (Cr), % | 15 to 17.5 | |
| 20 to 22.5 |
| Cobalt (Co), % | 0 | |
| 18.5 to 21 |
| Iron (Fe), % | 0 to 2.0 | |
| 24.3 to 36.2 |
| Manganese (Mn), % | 0 to 1.0 | |
| 1.0 to 2.0 |
| Molybdenum (Mo), % | 15 to 17.5 | |
| 2.5 to 3.5 |
| Nickel (Ni), % | 60.1 to 70 | |
| 19 to 21 |
| Niobium (Nb), % | 0 | |
| 0.75 to 1.3 |
| Nitrogen (N), % | 0 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.8 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tantalum (Ta), % | 0 | |
| 0.75 to 1.3 |
| Tungsten (W), % | 0 to 1.0 | |
| 2.0 to 3.0 |