Grade CX2M Nickel vs. ASTM A369 Grade FP92
Grade CX2M nickel belongs to the nickel alloys classification, while ASTM A369 grade FP92 belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is grade CX2M nickel and the bottom bar is ASTM A369 grade FP92.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 45 | |
| 19 |
| Fatigue Strength, MPa | 260 | |
| 330 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 84 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 550 | |
| 710 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 990 | |
| 590 |
| Melting Completion (Liquidus), °C | 1500 | |
| 1490 |
| Melting Onset (Solidus), °C | 1450 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 470 |
| Thermal Conductivity, W/m-K | 10 | |
| 26 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 11 |
| Density, g/cm3 | 8.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 2.8 |
| Embodied Energy, MJ/kg | 160 | |
| 40 |
| Embodied Water, L/kg | 310 | |
| 89 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 210 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 | |
| 620 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 18 | |
| 25 |
| Strength to Weight: Bending, points | 17 | |
| 22 |
| Thermal Diffusivity, mm2/s | 2.7 | |
| 6.9 |
| Thermal Shock Resistance, points | 15 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.020 |
| Boron (B), % | 0 | |
| 0.0010 to 0.0060 |
| Carbon (C), % | 0 to 0.020 | |
| 0.070 to 0.13 |
| Chromium (Cr), % | 22 to 24 | |
| 8.5 to 9.5 |
| Iron (Fe), % | 0 to 1.5 | |
| 85.8 to 89.1 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 15 to 16.5 | |
| 0.3 to 0.6 |
| Nickel (Ni), % | 56.4 to 63 | |
| 0 to 0.4 |
| Niobium (Nb), % | 0 | |
| 0.040 to 0.090 |
| Nitrogen (N), % | 0 | |
| 0.030 to 0.070 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 1.5 to 2.0 |
| Vanadium (V), % | 0 | |
| 0.15 to 0.25 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.010 |