Grade CX2M Nickel vs. SAE-AISI F2 Steel

Grade CX2M nickel belongs to the nickel alloys classification, while SAE-AISI F2 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is grade CX2M nickel and the bottom bar is SAE-AISI F2 steel.

Grade CX2M (N26059) Cast Nickel SAE-AISI F2 (T60602) Low-Alloy Tool Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.29
Poisson's Ratio		0.29

Shear Modulus, GPa		84
Shear Modulus, GPa		73

Tensile Strength: Ultimate (UTS), MPa		550
Tensile Strength: Ultimate (UTS), MPa		710 to 2360

Thermal Properties

Latent Heat of Fusion, J/g		330
Latent Heat of Fusion, J/g		250

Melting Completion (Liquidus), °C		1500
Melting Completion (Liquidus), °C		1520

Melting Onset (Solidus), °C		1450
Melting Onset (Solidus), °C		1470

Specific Heat Capacity, J/kg-K		430
Specific Heat Capacity, J/kg-K		460

Thermal Conductivity, W/m-K		10
Thermal Conductivity, W/m-K		42

Thermal Expansion, µm/m-K		12
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Base Metal Price, % relative		65
Base Metal Price, % relative		10

Density, g/cm³		8.7
Density, g/cm³		8.1

Embodied Carbon, kg CO₂/kg material		12
Embodied Carbon, kg CO₂/kg material		2.3

Embodied Energy, MJ/kg		160
Embodied Energy, MJ/kg		32

Embodied Water, L/kg		310
Embodied Water, L/kg		50

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		18
Strength to Weight: Axial, points		24 to 81

Strength to Weight: Bending, points		17
Strength to Weight: Bending, points		22 to 49

Thermal Diffusivity, mm²/s		2.7
Thermal Diffusivity, mm²/s		11

Thermal Shock Resistance, points		15
Thermal Shock Resistance, points		21 to 71

Alloy Composition

Carbon (C), %		0 to 0.020
Carbon (C), %		1.2 to 1.4

Chromium (Cr), %		22 to 24
Chromium (Cr), %		0.2 to 0.4

Iron (Fe), %		0 to 1.5
Iron (Fe), %		92.6 to 95.4

Manganese (Mn), %		0 to 1.0
Manganese (Mn), %		0.1 to 0.5

Molybdenum (Mo), %		15 to 16.5
Molybdenum (Mo), %		0

Nickel (Ni), %		56.4 to 63
Nickel (Ni), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 0.5
Silicon (Si), %		0.1 to 0.5

Sulfur (S), %		0 to 0.020
Sulfur (S), %		0 to 0.030

Tungsten (W), %		0
Tungsten (W), %		3.0 to 4.5