Grade FDC Steel vs. Grade 11 Titanium
Grade FDC steel belongs to the iron alloys classification, while grade 11 titanium belongs to the titanium alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is grade FDC steel and the bottom bar is grade 11 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 510 | |
| 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Reduction in Area, % | 42 | |
| 37 |
| Shear Modulus, GPa | 80 | |
| 38 |
| Tensile Strength: Ultimate (UTS), MPa | 1680 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 320 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1660 |
| Melting Onset (Solidus), °C | 1410 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 540 |
| Thermal Conductivity, W/m-K | 51 | |
| 22 |
| Thermal Expansion, µm/m-K | 13 | |
| 9.2 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 3.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 7.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 47 |
| Embodied Energy, MJ/kg | 19 | |
| 800 |
| Embodied Water, L/kg | 47 | |
| 470 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 35 |
| Strength to Weight: Axial, points | 60 | |
| 19 |
| Strength to Weight: Bending, points | 40 | |
| 22 |
| Thermal Diffusivity, mm2/s | 14 | |
| 8.9 |
| Thermal Shock Resistance, points | 50 | |
| 22 |
Alloy Composition
| Carbon (C), % | 0.6 to 0.75 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.12 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 98 to 99.4 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0.5 to 1.2 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.18 |
| Palladium (Pd), % | 0 | |
| 0.12 to 0.25 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0.1 to 0.35 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 98.8 to 99.88 |
| Residuals, % | 0 | |
| 0 to 0.4 |