Grade FDCrV Steel vs. SAE-AISI 1015 Steel
Both grade FDCrV steel and SAE-AISI 1015 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is grade FDCrV steel and the bottom bar is SAE-AISI 1015 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 540 | |
| 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 42 | |
| 46 to 56 |
| Shear Modulus, GPa | 80 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 1800 | |
| 390 to 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 400 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1470 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 48 | |
| 52 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 7.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 26 | |
| 18 |
| Embodied Water, L/kg | 49 | |
| 45 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 64 | |
| 14 to 15 |
| Strength to Weight: Bending, points | 42 | |
| 15 to 16 |
| Thermal Diffusivity, mm2/s | 13 | |
| 14 |
| Thermal Shock Resistance, points | 53 | |
| 12 to 14 |
Alloy Composition
| Carbon (C), % | 0.62 to 0.72 | |
| 0.13 to 0.18 |
| Chromium (Cr), % | 0.4 to 0.6 | |
| 0 |
| Copper (Cu), % | 0 to 0.12 | |
| 0 |
| Iron (Fe), % | 97.8 to 98.8 | |
| 99.13 to 99.57 |
| Manganese (Mn), % | 0.5 to 0.9 | |
| 0.3 to 0.6 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.15 to 0.3 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.050 |
| Vanadium (V), % | 0.15 to 0.25 | |
| 0 |