Grade FDSiCr Steel vs. EN 2.4665 Nickel
Grade FDSiCr steel belongs to the iron alloys classification, while EN 2.4665 nickel belongs to the nickel alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is grade FDSiCr steel and the bottom bar is EN 2.4665 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 80 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 1930 | |
| 790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 990 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Conductivity, W/m-K | 48 | |
| 12 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.2 | |
| 55 |
| Density, g/cm3 | 7.7 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 9.2 |
| Embodied Energy, MJ/kg | 20 | |
| 130 |
| Embodied Water, L/kg | 48 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 69 | |
| 26 |
| Strength to Weight: Bending, points | 44 | |
| 22 |
| Thermal Diffusivity, mm2/s | 13 | |
| 3.2 |
| Thermal Shock Resistance, points | 58 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.5 |
| Boron (B), % | 0 | |
| 0 to 0.010 |
| Carbon (C), % | 0.5 to 0.6 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 0.5 to 0.8 | |
| 20.5 to 23 |
| Cobalt (Co), % | 0 | |
| 0.5 to 2.5 |
| Copper (Cu), % | 0 to 0.12 | |
| 0 to 0.5 |
| Iron (Fe), % | 96.5 to 97.8 | |
| 17 to 20 |
| Manganese (Mn), % | 0.5 to 0.9 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 8.0 to 10 |
| Nickel (Ni), % | 0 | |
| 40.3 to 53.8 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.020 |
| Silicon (Si), % | 1.2 to 1.6 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 | |
| 0.2 to 1.0 |