MakeItFrom.com
Menu (ESC)

Grade FDSiCrV Steel vs. Z20301 Zinc

Grade FDSiCrV steel belongs to the iron alloys classification, while Z20301 zinc belongs to the zinc alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is grade FDSiCrV steel and the bottom bar is Z20301 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
87
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 80
35
Tensile Strength: Ultimate (UTS), MPa 2100
160

Thermal Properties

Latent Heat of Fusion, J/g 270
110
Maximum Temperature: Mechanical, °C 420
90
Melting Completion (Liquidus), °C 1440
410
Melting Onset (Solidus), °C 1400
400
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 47
110
Thermal Expansion, µm/m-K 13
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
37

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
11
Density, g/cm3 7.7
6.6
Embodied Carbon, kg CO2/kg material 1.9
2.8
Embodied Energy, MJ/kg 26
53
Embodied Water, L/kg 50
340

Common Calculations

Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 75
6.7
Strength to Weight: Bending, points 47
9.9
Thermal Diffusivity, mm2/s 13
44
Thermal Shock Resistance, points 63
5.0

Alloy Composition

Aluminum (Al), % 0
0 to 0.0020
Cadmium (Cd), % 0
0 to 0.010
Carbon (C), % 0.5 to 0.7
0
Chromium (Cr), % 0.5 to 1.0
0
Copper (Cu), % 0 to 0.12
0 to 0.0050
Iron (Fe), % 96 to 97.8
0 to 0.010
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0.4 to 0.9
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 1.2 to 1.7
0
Sulfur (S), % 0 to 0.025
0
Titanium (Ti), % 0
0 to 0.020
Vanadium (V), % 0.1 to 0.25
0
Zinc (Zn), % 0
99.853 to 100