Grade M30C Nickel vs. C14300 Copper
Grade M30C nickel belongs to the nickel alloys classification, while C14300 copper belongs to the copper alloys. They have a modest 30% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is grade M30C nickel and the bottom bar is C14300 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 160 | |
| 120 |
| Elongation at Break, % | 29 | |
| 2.0 to 42 |
| Poisson's Ratio | 0.32 | |
| 0.34 |
| Shear Modulus, GPa | 61 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 510 | |
| 220 to 460 |
| Tensile Strength: Yield (Proof), MPa | 250 | |
| 76 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 220 |
| Melting Completion (Liquidus), °C | 1290 | |
| 1080 |
| Melting Onset (Solidus), °C | 1240 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 390 |
| Thermal Conductivity, W/m-K | 22 | |
| 380 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.3 | |
| 96 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.4 | |
| 96 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 31 |
| Density, g/cm3 | 8.8 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 9.5 | |
| 2.6 |
| Embodied Energy, MJ/kg | 140 | |
| 41 |
| Embodied Water, L/kg | 250 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 9.0 to 72 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 | |
| 25 to 810 |
| Stiffness to Weight: Axial, points | 10 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 21 | |
| 18 |
| Strength to Weight: Axial, points | 16 | |
| 6.8 to 14 |
| Strength to Weight: Bending, points | 16 | |
| 9.1 to 15 |
| Thermal Diffusivity, mm2/s | 5.7 | |
| 110 |
| Thermal Shock Resistance, points | 18 | |
| 7.8 to 16 |
Alloy Composition
| Cadmium (Cd), % | 0 | |
| 0.050 to 0.15 |
| Carbon (C), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 26 to 33 | |
| 99.9 to 99.95 |
| Iron (Fe), % | 0 to 3.5 | |
| 0 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 |
| Nickel (Ni), % | 56.6 to 72 | |
| 0 |
| Niobium (Nb), % | 1.0 to 3.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 1.0 to 2.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |