Grade M30H Nickel vs. Grade 705C Zirconium

Grade M30H nickel belongs to the nickel alloys classification, while grade 705C zirconium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade M30H nickel and the bottom bar is grade 705C zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 160
98
Elongation at Break, % 11
13
Poisson's Ratio 0.32
0.34
Shear Modulus, GPa 61
36
Tensile Strength: Ultimate (UTS), MPa 770
540
Tensile Strength: Yield (Proof), MPa 470
390

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Specific Heat Capacity, J/kg-K 440
270
Thermal Conductivity, W/m-K 22
18
Thermal Expansion, µm/m-K 13
5.7

Otherwise Unclassified Properties

Density, g/cm3 8.6
6.7
Embodied Water, L/kg 250
450

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
66
Resilience: Unit (Modulus of Resilience), kJ/m3 700
790
Stiffness to Weight: Axial, points 10
8.1
Stiffness to Weight: Bending, points 21
23
Strength to Weight: Axial, points 25
22
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 5.7
9.9
Thermal Shock Resistance, points 27
69

Alloy Composition

Carbon (C), % 0 to 0.3
0 to 0.1
Copper (Cu), % 27 to 33
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 0 to 3.5
0 to 0.3
Manganese (Mn), % 0 to 1.5
0
Nickel (Ni), % 57.9 to 70.3
0
Niobium (Nb), % 0
2.0 to 3.0
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.010
Silicon (Si), % 2.7 to 3.7
0
Sulfur (S), % 0 to 0.030
0
Zirconium (Zr), % 0
91.9 to 98