Grade N12MV Nickel vs. AISI 308 Stainless Steel

Grade N12MV nickel belongs to the nickel alloys classification, while AISI 308 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade N12MV nickel and the bottom bar is AISI 308 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 6.8
45
Fatigue Strength, MPa 130
210
Poisson's Ratio 0.31
0.28
Shear Modulus, GPa 84
78
Tensile Strength: Ultimate (UTS), MPa 600
590
Tensile Strength: Yield (Proof), MPa 310
230

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Maximum Temperature: Mechanical, °C 900
990
Melting Completion (Liquidus), °C 1620
1420
Melting Onset (Solidus), °C 1570
1380
Specific Heat Capacity, J/kg-K 390
480
Thermal Expansion, µm/m-K 10
16

Otherwise Unclassified Properties

Base Metal Price, % relative 75
17
Density, g/cm3 9.2
7.8
Embodied Carbon, kg CO2/kg material 16
3.2
Embodied Energy, MJ/kg 200
46
Embodied Water, L/kg 260
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 34
210
Resilience: Unit (Modulus of Resilience), kJ/m3 220
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 22
25
Strength to Weight: Axial, points 18
21
Strength to Weight: Bending, points 17
20
Thermal Shock Resistance, points 19
13

Alloy Composition

Carbon (C), % 0 to 0.12
0 to 0.080
Chromium (Cr), % 0 to 1.0
19 to 21
Iron (Fe), % 4.0 to 6.0
64.1 to 71
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 26 to 30
0
Nickel (Ni), % 60.2 to 69.8
10 to 12
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0.2 to 0.6
0