Grade N12MV Nickel vs. EN 1.4520 Stainless Steel

Grade N12MV nickel belongs to the nickel alloys classification, while EN 1.4520 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is grade N12MV nickel and the bottom bar is EN 1.4520 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 6.8
26
Fatigue Strength, MPa 130
160
Poisson's Ratio 0.31
0.28
Shear Modulus, GPa 84
77
Tensile Strength: Ultimate (UTS), MPa 600
480
Tensile Strength: Yield (Proof), MPa 310
220

Thermal Properties

Latent Heat of Fusion, J/g 320
280
Maximum Temperature: Mechanical, °C 900
870
Melting Completion (Liquidus), °C 1620
1440
Melting Onset (Solidus), °C 1570
1400
Specific Heat Capacity, J/kg-K 390
480
Thermal Expansion, µm/m-K 10
10

Otherwise Unclassified Properties

Base Metal Price, % relative 75
8.5
Density, g/cm3 9.2
7.7
Embodied Carbon, kg CO2/kg material 16
2.2
Embodied Energy, MJ/kg 200
32
Embodied Water, L/kg 260
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 34
100
Resilience: Unit (Modulus of Resilience), kJ/m3 220
120
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 22
25
Strength to Weight: Axial, points 18
17
Strength to Weight: Bending, points 17
18
Thermal Shock Resistance, points 19
17

Alloy Composition

Carbon (C), % 0 to 0.12
0 to 0.025
Chromium (Cr), % 0 to 1.0
16 to 18
Iron (Fe), % 4.0 to 6.0
80.1 to 83.9
Manganese (Mn), % 0 to 1.0
0 to 0.5
Molybdenum (Mo), % 26 to 30
0
Nickel (Ni), % 60.2 to 69.8
0
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.8
Vanadium (V), % 0.2 to 0.6
0