Grade N12MV Nickel vs. Solder Alloy 201

Grade N12MV nickel belongs to the nickel alloys classification, while solder alloy 201 belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade N12MV nickel and the bottom bar is solder alloy 201.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
50
Elongation at Break, % 6.8
38
Poisson's Ratio 0.31
0.35
Shear Modulus, GPa 84
19
Tensile Strength: Ultimate (UTS), MPa 600
41

Thermal Properties

Latent Heat of Fusion, J/g 320
64
Melting Completion (Liquidus), °C 1620
240
Melting Onset (Solidus), °C 1570
240
Specific Heat Capacity, J/kg-K 390
220
Thermal Expansion, µm/m-K 10
21

Otherwise Unclassified Properties

Density, g/cm3 9.2
7.3
Embodied Carbon, kg CO2/kg material 16
15
Embodied Energy, MJ/kg 200
250
Embodied Water, L/kg 260
1320

Common Calculations

Stiffness to Weight: Axial, points 13
3.8
Stiffness to Weight: Bending, points 22
17
Strength to Weight: Axial, points 18
1.6
Strength to Weight: Bending, points 17
3.6
Thermal Shock Resistance, points 19
2.7

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
4.5 to 5.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.12
0
Chromium (Cr), % 0 to 1.0
0
Copper (Cu), % 0
0 to 0.050
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 4.0 to 6.0
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 26 to 30
0
Nickel (Ni), % 60.2 to 69.8
0 to 0.010
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
94 to 95.5
Vanadium (V), % 0.2 to 0.6
0
Zinc (Zn), % 0
0 to 0.0010