Grade N12MV Nickel vs. SAE-AISI H25 Steel

Grade N12MV nickel belongs to the nickel alloys classification, while SAE-AISI H25 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is grade N12MV nickel and the bottom bar is SAE-AISI H25 steel.

Grade N12MV (J30012) Cast Nickel SAE-AISI H25 (T20825) Tungsten Hot-Work Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.31
Poisson's Ratio		0.29

Shear Modulus, GPa		84
Shear Modulus, GPa		79

Tensile Strength: Ultimate (UTS), MPa		600
Tensile Strength: Ultimate (UTS), MPa		710 to 1620

Thermal Properties

Latent Heat of Fusion, J/g		320
Latent Heat of Fusion, J/g		250

Melting Completion (Liquidus), °C		1620
Melting Completion (Liquidus), °C		1750

Melting Onset (Solidus), °C		1570
Melting Onset (Solidus), °C		1700

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		420

Thermal Expansion, µm/m-K		10
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		75
Base Metal Price, % relative		38

Density, g/cm³		9.2
Density, g/cm³		9.1

Embodied Carbon, kg CO₂/kg material		16
Embodied Carbon, kg CO₂/kg material		6.2

Embodied Energy, MJ/kg		200
Embodied Energy, MJ/kg		93

Embodied Water, L/kg		260
Embodied Water, L/kg		83

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		12

Stiffness to Weight: Bending, points		22
Stiffness to Weight: Bending, points		22

Strength to Weight: Axial, points		18
Strength to Weight: Axial, points		22 to 50

Strength to Weight: Bending, points		17
Strength to Weight: Bending, points		20 to 34

Thermal Shock Resistance, points		19
Thermal Shock Resistance, points		22 to 49

Alloy Composition

Carbon (C), %		0 to 0.12
Carbon (C), %		0.22 to 0.32

Chromium (Cr), %		0 to 1.0
Chromium (Cr), %		3.8 to 4.5

Copper (Cu), %		0
Copper (Cu), %		0 to 0.25

Iron (Fe), %		4.0 to 6.0
Iron (Fe), %		77.2 to 81.3

Manganese (Mn), %		0 to 1.0
Manganese (Mn), %		0.15 to 0.4

Molybdenum (Mo), %		26 to 30
Molybdenum (Mo), %		0

Nickel (Ni), %		60.2 to 69.8
Nickel (Ni), %		0 to 0.3

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0.15 to 0.4

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030

Tungsten (W), %		0
Tungsten (W), %		14 to 16

Vanadium (V), %		0.2 to 0.6
Vanadium (V), %		0.4 to 0.6