Grade N12MV Nickel vs. Sintered 6061 Aluminum

Grade N12MV nickel belongs to the nickel alloys classification, while sintered 6061 aluminum belongs to the aluminum alloys. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is grade N12MV nickel and the bottom bar is sintered 6061 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
68
Elongation at Break, % 6.8
0.5 to 6.0
Fatigue Strength, MPa 130
32 to 62
Poisson's Ratio 0.31
0.33
Shear Modulus, GPa 84
25
Tensile Strength: Ultimate (UTS), MPa 600
83 to 210
Tensile Strength: Yield (Proof), MPa 310
62 to 190

Thermal Properties

Latent Heat of Fusion, J/g 320
400
Maximum Temperature: Mechanical, °C 900
170
Melting Completion (Liquidus), °C 1620
640
Melting Onset (Solidus), °C 1570
610
Specific Heat Capacity, J/kg-K 390
900
Thermal Expansion, µm/m-K 10
23

Otherwise Unclassified Properties

Base Metal Price, % relative 75
9.5
Density, g/cm3 9.2
2.7
Embodied Carbon, kg CO2/kg material 16
8.3
Embodied Energy, MJ/kg 200
150
Embodied Water, L/kg 260
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 34
0.68 to 7.0
Resilience: Unit (Modulus of Resilience), kJ/m3 220
28 to 280
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 22
51
Strength to Weight: Axial, points 18
8.6 to 21
Strength to Weight: Bending, points 17
16 to 29
Thermal Shock Resistance, points 19
3.8 to 9.4

Alloy Composition

Aluminum (Al), % 0
96 to 99.4
Carbon (C), % 0 to 0.12
0
Chromium (Cr), % 0 to 1.0
0
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 4.0 to 6.0
0
Magnesium (Mg), % 0
0.4 to 1.2
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 26 to 30
0
Nickel (Ni), % 60.2 to 69.8
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0.2 to 0.8
Sulfur (S), % 0 to 0.030
0
Vanadium (V), % 0.2 to 0.6
0
Residuals, % 0
0 to 1.5