Grade N7M Nickel vs. SAE-AISI M1 Steel

Grade N7M nickel belongs to the nickel alloys classification, while SAE-AISI M1 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is grade N7M nickel and the bottom bar is SAE-AISI M1 steel.

Grade N7M (J30007) Cast Nickel SAE-AISI M1 (T11301) Molybdenum High-Speed Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.31
Poisson's Ratio		0.29

Shear Modulus, GPa		85
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		590
Tensile Strength: Ultimate (UTS), MPa		730 to 2140

Thermal Properties

Latent Heat of Fusion, J/g		320
Latent Heat of Fusion, J/g		270

Melting Completion (Liquidus), °C		1650
Melting Completion (Liquidus), °C		1560

Melting Onset (Solidus), °C		1590
Melting Onset (Solidus), °C		1510

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		450

Thermal Expansion, µm/m-K		9.9
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		75
Base Metal Price, % relative		18

Density, g/cm³		9.3
Density, g/cm³		8.1

Embodied Carbon, kg CO₂/kg material		16
Embodied Carbon, kg CO₂/kg material		7.0

Embodied Energy, MJ/kg		200
Embodied Energy, MJ/kg		99

Embodied Water, L/kg		270
Embodied Water, L/kg		98

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		22
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		18
Strength to Weight: Axial, points		25 to 73

Strength to Weight: Bending, points		17
Strength to Weight: Bending, points		22 to 45

Thermal Shock Resistance, points		19
Thermal Shock Resistance, points		23 to 66

Alloy Composition

Carbon (C), %		0 to 0.070
Carbon (C), %		0.78 to 0.88

Chromium (Cr), %		0 to 1.0
Chromium (Cr), %		3.5 to 4.0

Copper (Cu), %		0
Copper (Cu), %		0 to 0.25

Iron (Fe), %		0 to 3.0
Iron (Fe), %		81 to 84.8

Manganese (Mn), %		0 to 1.0
Manganese (Mn), %		0.15 to 0.4

Molybdenum (Mo), %		30 to 33
Molybdenum (Mo), %		8.2 to 9.2

Nickel (Ni), %		60.9 to 70
Nickel (Ni), %		0 to 0.3

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0.2 to 0.5

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030

Tungsten (W), %		0
Tungsten (W), %		1.4 to 2.1

Vanadium (V), %		0
Vanadium (V), %		1.0 to 1.4