Grade TDCrV Steel vs. EN 1.4818 Stainless Steel
Both grade TDCrV steel and EN 1.4818 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is grade TDCrV steel and the bottom bar is EN 1.4818 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 520 | |
| 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 80 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 1730 | |
| 700 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 1050 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1410 |
| Melting Onset (Solidus), °C | 1410 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 490 |
| Thermal Conductivity, W/m-K | 49 | |
| 17 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 2.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 16 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 3.1 |
| Embodied Energy, MJ/kg | 26 | |
| 44 |
| Embodied Water, L/kg | 49 | |
| 150 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 61 | |
| 25 |
| Strength to Weight: Bending, points | 41 | |
| 23 |
| Thermal Diffusivity, mm2/s | 13 | |
| 4.5 |
| Thermal Shock Resistance, points | 51 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0.62 to 0.72 | |
| 0.040 to 0.080 |
| Cerium (Ce), % | 0 | |
| 0.030 to 0.080 |
| Chromium (Cr), % | 0.4 to 0.6 | |
| 18 to 20 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 97.8 to 98.8 | |
| 65.6 to 71.8 |
| Manganese (Mn), % | 0.5 to 0.9 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 9.0 to 11 |
| Nitrogen (N), % | 0 | |
| 0.12 to 0.2 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.045 |
| Silicon (Si), % | 0.15 to 0.3 | |
| 1.0 to 2.0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.015 |
| Vanadium (V), % | 0.15 to 0.25 | |
| 0 |