Grade TDCrV Steel vs. Solder Alloy 136

Grade TDCrV steel belongs to the iron alloys classification, while solder alloy 136 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is grade TDCrV steel and the bottom bar is solder alloy 136.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
25
Poisson's Ratio 0.29
0.42
Shear Modulus, GPa 80
8.9
Tensile Strength: Ultimate (UTS), MPa 1730
34

Thermal Properties

Latent Heat of Fusion, J/g 250
34
Melting Completion (Liquidus), °C 1450
260
Melting Onset (Solidus), °C 1410
190
Specific Heat Capacity, J/kg-K 470
150
Thermal Conductivity, W/m-K 49
40
Thermal Expansion, µm/m-K 13
27

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
9.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
90
Density, g/cm3 7.8
10
Embodied Carbon, kg CO2/kg material 1.9
6.8
Embodied Energy, MJ/kg 26
110
Embodied Water, L/kg 49
680

Common Calculations

Stiffness to Weight: Axial, points 13
1.4
Stiffness to Weight: Bending, points 24
9.5
Strength to Weight: Axial, points 61
0.92
Strength to Weight: Bending, points 41
2.3
Thermal Diffusivity, mm2/s 13
26
Thermal Shock Resistance, points 51
3.6

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0.5 to 2.0
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0.62 to 0.72
0
Chromium (Cr), % 0.4 to 0.6
0
Copper (Cu), % 0 to 0.1
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 97.8 to 98.8
0 to 0.020
Lead (Pb), % 0
71.9 to 75
Manganese (Mn), % 0.5 to 0.9
0
Nickel (Ni), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0.15 to 0.3
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.020
0
Tin (Sn), % 0
24.5 to 25.5
Vanadium (V), % 0.15 to 0.25
0
Zinc (Zn), % 0
0 to 0.0010