Grade TDSiCr Steel vs. AISI 329 Stainless Steel

Both grade TDSiCr steel and AISI 329 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade TDSiCr steel and the bottom bar is AISI 329 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 590
240
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 80
80
Tensile Strength: Ultimate (UTS), MPa 1950
710

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Maximum Temperature: Mechanical, °C 410
1100
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 46
16
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
16
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 1.5
3.1
Embodied Energy, MJ/kg 20
44
Embodied Water, L/kg 48
170

Common Calculations

Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 70
25
Strength to Weight: Bending, points 45
23
Thermal Diffusivity, mm2/s 12
4.3
Thermal Shock Resistance, points 58
19

Alloy Composition

Carbon (C), % 0.5 to 0.6
0 to 0.080
Chromium (Cr), % 0.5 to 0.8
23 to 28
Copper (Cu), % 0 to 0.1
0
Iron (Fe), % 96.6 to 97.8
63.1 to 74
Manganese (Mn), % 0.5 to 0.9
0 to 1.0
Molybdenum (Mo), % 0
1.0 to 2.0
Nickel (Ni), % 0
2.0 to 5.0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 1.2 to 1.6
0 to 0.75
Sulfur (S), % 0 to 0.020
0 to 0.030