Grade Ti-Pd17 Titanium vs. EN 1.1132 Steel
Grade Ti-Pd17 titanium belongs to the titanium alloys classification, while EN 1.1132 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is grade Ti-Pd17 titanium and the bottom bar is EN 1.1132 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 | |
| 110 to 140 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 22 | |
| 12 to 24 |
| Fatigue Strength, MPa | 140 | |
| 180 to 280 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 370 to 490 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 240 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 400 |
| Melting Completion (Liquidus), °C | 1660 | |
| 1460 |
| Melting Onset (Solidus), °C | 1610 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 470 |
| Thermal Conductivity, W/m-K | 21 | |
| 51 |
| Thermal Expansion, µm/m-K | 8.7 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.6 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.1 | |
| 8.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 36 | |
| 1.4 |
| Embodied Energy, MJ/kg | 600 | |
| 18 |
| Embodied Water, L/kg | 230 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 55 | |
| 38 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 160 to 430 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 35 | |
| 24 |
| Strength to Weight: Axial, points | 17 | |
| 13 to 17 |
| Strength to Weight: Bending, points | 21 | |
| 15 to 18 |
| Thermal Diffusivity, mm2/s | 8.8 | |
| 14 |
| Thermal Shock Resistance, points | 21 | |
| 12 to 16 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0.13 to 0.17 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 98.6 to 99.57 |
| Manganese (Mn), % | 0 | |
| 0.3 to 0.6 |
| Nickel (Ni), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.25 | |
| 0 |
| Palladium (Pd), % | 0.040 to 0.080 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Titanium (Ti), % | 98.9 to 99.96 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |