Grade Ti-Pd18 Titanium vs. SAE-AISI 1212 Steel

Grade Ti-Pd18 titanium belongs to the titanium alloys classification, while SAE-AISI 1212 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is grade Ti-Pd18 titanium and the bottom bar is SAE-AISI 1212 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 320
140 to 180
Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 17
11 to 28
Fatigue Strength, MPa 350
200 to 290
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 40
73
Tensile Strength: Ultimate (UTS), MPa 710
440 to 620
Tensile Strength: Yield (Proof), MPa 540
260 to 460

Thermal Properties

Latent Heat of Fusion, J/g 410
250
Maximum Temperature: Mechanical, °C 330
400
Melting Completion (Liquidus), °C 1640
1460
Melting Onset (Solidus), °C 1590
1420
Specific Heat Capacity, J/kg-K 550
470
Thermal Conductivity, W/m-K 8.2
52
Thermal Expansion, µm/m-K 9.1
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.1

Otherwise Unclassified Properties

Density, g/cm3 4.5
7.8
Embodied Carbon, kg CO2/kg material 41
1.4
Embodied Energy, MJ/kg 670
18
Embodied Water, L/kg 270
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
64 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 1380
180 to 560
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 35
24
Strength to Weight: Axial, points 44
15 to 22
Strength to Weight: Bending, points 39
16 to 20
Thermal Diffusivity, mm2/s 3.3
14
Thermal Shock Resistance, points 52
14 to 20

Alloy Composition

Aluminum (Al), % 2.5 to 3.5
0
Carbon (C), % 0 to 0.1
0 to 0.13
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
98.5 to 99.07
Manganese (Mn), % 0
0.7 to 1.0
Nickel (Ni), % 0 to 0.050
0
Oxygen (O), % 0 to 0.15
0
Palladium (Pd), % 0.040 to 0.080
0
Phosphorus (P), % 0
0.070 to 0.12
Sulfur (S), % 0
0.16 to 0.23
Titanium (Ti), % 92.5 to 95.5
0
Vanadium (V), % 2.0 to 3.0
0
Residuals, % 0 to 0.4
0