Grade Ti-Pd18 Titanium vs. C92600 Bronze

Grade Ti-Pd18 titanium belongs to the titanium alloys classification, while C92600 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is grade Ti-Pd18 titanium and the bottom bar is C92600 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 320
70
Elastic (Young's, Tensile) Modulus, GPa 110
110
Elongation at Break, % 17
30
Poisson's Ratio 0.32
0.34
Shear Modulus, GPa 40
40
Tensile Strength: Ultimate (UTS), MPa 710
300
Tensile Strength: Yield (Proof), MPa 540
140

Thermal Properties

Latent Heat of Fusion, J/g 410
190
Maximum Temperature: Mechanical, °C 330
170
Melting Completion (Liquidus), °C 1640
980
Melting Onset (Solidus), °C 1590
840
Specific Heat Capacity, J/kg-K 550
370
Thermal Conductivity, W/m-K 8.2
67
Thermal Expansion, µm/m-K 9.1
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
9.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
9.3

Otherwise Unclassified Properties

Density, g/cm3 4.5
8.7
Embodied Carbon, kg CO2/kg material 41
3.6
Embodied Energy, MJ/kg 670
58
Embodied Water, L/kg 270
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
74
Resilience: Unit (Modulus of Resilience), kJ/m3 1380
88
Stiffness to Weight: Axial, points 13
6.8
Stiffness to Weight: Bending, points 35
18
Strength to Weight: Axial, points 44
9.6
Strength to Weight: Bending, points 39
11
Thermal Diffusivity, mm2/s 3.3
21
Thermal Shock Resistance, points 52
11

Alloy Composition

Aluminum (Al), % 2.5 to 3.5
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
86 to 88.5
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
0 to 0.2
Lead (Pb), % 0
0.8 to 1.5
Nickel (Ni), % 0 to 0.050
0 to 0.7
Oxygen (O), % 0 to 0.15
0
Palladium (Pd), % 0.040 to 0.080
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.0050
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0
9.3 to 10.5
Titanium (Ti), % 92.5 to 95.5
0
Vanadium (V), % 2.0 to 3.0
0
Zinc (Zn), % 0
1.3 to 2.5
Residuals, % 0
0 to 0.7