Grade Ti-Pd18 Titanium vs. C95200 Bronze

Grade Ti-Pd18 titanium belongs to the titanium alloys classification, while C95200 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is grade Ti-Pd18 titanium and the bottom bar is C95200 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 320
120
Elastic (Young's, Tensile) Modulus, GPa 110
110
Elongation at Break, % 17
29
Poisson's Ratio 0.32
0.34
Shear Modulus, GPa 40
42
Tensile Strength: Ultimate (UTS), MPa 710
520
Tensile Strength: Yield (Proof), MPa 540
190

Thermal Properties

Latent Heat of Fusion, J/g 410
230
Maximum Temperature: Mechanical, °C 330
220
Melting Completion (Liquidus), °C 1640
1050
Melting Onset (Solidus), °C 1590
1040
Specific Heat Capacity, J/kg-K 550
430
Thermal Conductivity, W/m-K 8.2
50
Thermal Expansion, µm/m-K 9.1
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
11
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
12

Otherwise Unclassified Properties

Density, g/cm3 4.5
8.3
Embodied Carbon, kg CO2/kg material 41
3.0
Embodied Energy, MJ/kg 670
50
Embodied Water, L/kg 270
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
120
Resilience: Unit (Modulus of Resilience), kJ/m3 1380
170
Stiffness to Weight: Axial, points 13
7.6
Stiffness to Weight: Bending, points 35
19
Strength to Weight: Axial, points 44
17
Strength to Weight: Bending, points 39
17
Thermal Diffusivity, mm2/s 3.3
14
Thermal Shock Resistance, points 52
19

Alloy Composition

Aluminum (Al), % 2.5 to 3.5
8.5 to 9.5
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
86 to 89
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
2.5 to 4.0
Nickel (Ni), % 0 to 0.050
0
Oxygen (O), % 0 to 0.15
0
Palladium (Pd), % 0.040 to 0.080
0
Titanium (Ti), % 92.5 to 95.5
0
Vanadium (V), % 2.0 to 3.0
0
Residuals, % 0
0 to 1.0