Grade Ti-Pd7B Titanium vs. Grade 2 Babbitt Metal
Grade Ti-Pd7B titanium belongs to the titanium alloys classification, while grade 2 Babbitt Metal belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is grade Ti-Pd7B titanium and the bottom bar is grade 2 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 180 | |
25 |
Elastic (Young's, Tensile) Modulus, GPa | 110 | |
53 |
Poisson's Ratio | 0.32 | |
0.35 |
Shear Modulus, GPa | 40 | |
19 |
Tensile Strength: Yield (Proof), MPa | 310 | |
42 |
Thermal Properties
Latent Heat of Fusion, J/g | 420 | |
72 |
Melting Completion (Liquidus), °C | 1660 | |
350 |
Melting Onset (Solidus), °C | 1610 | |
240 |
Specific Heat Capacity, J/kg-K | 540 | |
230 |
Thermal Expansion, µm/m-K | 8.7 | |
21 |
Otherwise Unclassified Properties
Density, g/cm3 | 4.5 | |
7.3 |
Embodied Carbon, kg CO2/kg material | 49 | |
12 |
Embodied Energy, MJ/kg | 840 | |
200 |
Embodied Water, L/kg | 520 | |
1240 |
Common Calculations
Resilience: Unit (Modulus of Resilience), kJ/m3 | 440 | |
17 |
Stiffness to Weight: Axial, points | 13 | |
4.0 |
Stiffness to Weight: Bending, points | 35 | |
17 |
Alloy Composition
Aluminum (Al), % | 0 | |
0 to 0.0050 |
Antimony (Sb), % | 0 | |
7.0 to 8.0 |
Arsenic (As), % | 0 | |
0 to 0.1 |
Bismuth (Bi), % | 0 | |
0 to 0.080 |
Cadmium (Cd), % | 0 | |
0 to 0.050 |
Carbon (C), % | 0 to 0.1 | |
0 |
Copper (Cu), % | 0 | |
3.0 to 4.0 |
Hydrogen (H), % | 0 to 0.015 | |
0 |
Iron (Fe), % | 0 to 0.2 | |
0 to 0.080 |
Lead (Pb), % | 0 | |
0 to 0.35 |
Nickel (Ni), % | 0 to 0.050 | |
0 |
Oxygen (O), % | 0 to 0.4 | |
0 |
Palladium (Pd), % | 0.12 to 0.3 | |
0 |
Tin (Sn), % | 0 | |
87.3 to 90 |
Titanium (Ti), % | 98.8 to 99.9 | |
0 |
Zinc (Zn), % | 0 | |
0 to 0.0050 |
Residuals, % | 0 to 0.4 | |
0 |