Grade Ti-Pd7B Titanium vs. Solder Alloy 131
Grade Ti-Pd7B titanium belongs to the titanium alloys classification, while solder alloy 131 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is grade Ti-Pd7B titanium and the bottom bar is solder alloy 131.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 110 | |
38 |
Elongation at Break, % | 17 | |
47 |
Poisson's Ratio | 0.32 | |
0.39 |
Shear Modulus, GPa | 40 | |
14 |
Tensile Strength: Ultimate (UTS), MPa | 390 | |
31 |
Thermal Properties
Latent Heat of Fusion, J/g | 420 | |
46 |
Melting Completion (Liquidus), °C | 1660 | |
180 |
Melting Onset (Solidus), °C | 1610 | |
180 |
Specific Heat Capacity, J/kg-K | 540 | |
190 |
Thermal Conductivity, W/m-K | 22 | |
55 |
Thermal Expansion, µm/m-K | 8.7 | |
25 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 3.6 | |
11 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 7.1 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 4.5 | |
8.8 |
Embodied Carbon, kg CO2/kg material | 49 | |
11 |
Embodied Energy, MJ/kg | 840 | |
180 |
Embodied Water, L/kg | 520 | |
940 |
Common Calculations
Stiffness to Weight: Axial, points | 13 | |
2.4 |
Stiffness to Weight: Bending, points | 35 | |
13 |
Strength to Weight: Axial, points | 24 | |
1.0 |
Strength to Weight: Bending, points | 26 | |
2.5 |
Thermal Diffusivity, mm2/s | 8.9 | |
33 |
Thermal Shock Resistance, points | 30 | |
2.4 |
Alloy Composition
Aluminum (Al), % | 0 | |
0 to 0.0010 |
Antimony (Sb), % | 0 | |
0.2 to 0.5 |
Arsenic (As), % | 0 | |
0 to 0.030 |
Bismuth (Bi), % | 0 | |
0 to 0.1 |
Cadmium (Cd), % | 0 | |
0 to 0.0020 |
Carbon (C), % | 0 to 0.1 | |
0 |
Copper (Cu), % | 0 | |
0 to 0.080 |
Gold (Au), % | 0 | |
0 to 0.050 |
Hydrogen (H), % | 0 to 0.015 | |
0 |
Indium (In), % | 0 | |
0 to 0.1 |
Iron (Fe), % | 0 to 0.2 | |
0 to 0.020 |
Lead (Pb), % | 0 | |
35.5 to 37.3 |
Nickel (Ni), % | 0 to 0.050 | |
0 to 0.010 |
Oxygen (O), % | 0 to 0.4 | |
0 |
Palladium (Pd), % | 0.12 to 0.3 | |
0 |
Silver (Ag), % | 0 | |
0 to 0.1 |
Tin (Sn), % | 0 | |
62.5 to 63.5 |
Titanium (Ti), % | 98.8 to 99.9 | |
0 |
Zinc (Zn), % | 0 | |
0 to 0.0010 |
Residuals, % | 0 to 0.4 | |
0 |