Grade Ti-Pd8A Titanium vs. ASTM A225 Steel
Grade Ti-Pd8A titanium belongs to the titanium alloys classification, while ASTM A225 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is grade Ti-Pd8A titanium and the bottom bar is ASTM A225 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 | |
| 190 to 250 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 13 | |
| 21 to 23 |
| Fatigue Strength, MPa | 260 | |
| 330 to 390 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 500 | |
| 620 to 830 |
| Tensile Strength: Yield (Proof), MPa | 430 | |
| 460 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 400 |
| Melting Completion (Liquidus), °C | 1660 | |
| 1460 |
| Melting Onset (Solidus), °C | 1610 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 470 |
| Thermal Conductivity, W/m-K | 21 | |
| 52 |
| Thermal Expansion, µm/m-K | 8.7 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.5 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.9 | |
| 8.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 49 | |
| 1.8 |
| Embodied Energy, MJ/kg | 840 | |
| 24 to 25 |
| Embodied Water, L/kg | 520 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 65 | |
| 120 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 880 | |
| 580 to 820 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 35 | |
| 24 |
| Strength to Weight: Axial, points | 31 | |
| 22 to 29 |
| Strength to Weight: Bending, points | 31 | |
| 21 to 25 |
| Thermal Diffusivity, mm2/s | 8.6 | |
| 14 |
| Thermal Shock Resistance, points | 39 | |
| 18 to 24 |