Grade VDC Steel vs. EN 1.1203 Steel
Both grade VDC steel and EN 1.1203 steel are iron alloys. Their average alloy composition is basically identical. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is grade VDC steel and the bottom bar is EN 1.1203 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 510 | |
| 200 to 230 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 80 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 1700 | |
| 690 to 780 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 48 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 2.1 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 47 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 60 | |
| 25 to 28 |
| Strength to Weight: Bending, points | 40 | |
| 22 to 24 |
| Thermal Diffusivity, mm2/s | 14 | |
| 13 |
| Thermal Shock Resistance, points | 50 | |
| 22 to 25 |
Alloy Composition
| Carbon (C), % | 0.6 to 0.75 | |
| 0.52 to 0.6 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 to 0.4 |
| Copper (Cu), % | 0 to 0.060 | |
| 0 |
| Iron (Fe), % | 98.3 to 99.35 | |
| 97.1 to 98.9 |
| Manganese (Mn), % | 0.5 to 1.0 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 0 to 0.4 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.035 |
| Silicon (Si), % | 0.15 to 0.3 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.035 |