Grade VDCrV Steel vs. 5182 Aluminum

Grade VDCrV steel belongs to the iron alloys classification, while 5182 aluminum belongs to the aluminum alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is grade VDCrV steel and the bottom bar is 5182 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
68
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 80
25
Tensile Strength: Ultimate (UTS), MPa 1730
280 to 420

Thermal Properties

Latent Heat of Fusion, J/g 250
390
Maximum Temperature: Mechanical, °C 410
180
Melting Completion (Liquidus), °C 1450
640
Melting Onset (Solidus), °C 1410
590
Specific Heat Capacity, J/kg-K 470
900
Thermal Conductivity, W/m-K 49
130
Thermal Expansion, µm/m-K 13
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
28
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
94

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
9.5
Density, g/cm3 7.8
2.7
Embodied Carbon, kg CO2/kg material 1.9
8.9
Embodied Energy, MJ/kg 26
150
Embodied Water, L/kg 49
1180

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
51
Strength to Weight: Axial, points 61
29 to 44
Strength to Weight: Bending, points 41
36 to 47
Thermal Diffusivity, mm2/s 13
53
Thermal Shock Resistance, points 51
12 to 19

Alloy Composition

Aluminum (Al), % 0
93.2 to 95.8
Carbon (C), % 0.62 to 0.72
0
Chromium (Cr), % 0.4 to 0.6
0 to 0.1
Copper (Cu), % 0 to 0.060
0 to 0.15
Iron (Fe), % 97.8 to 98.8
0 to 0.35
Magnesium (Mg), % 0
4.0 to 5.0
Manganese (Mn), % 0.5 to 0.9
0.2 to 0.5
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0.15 to 0.3
0 to 0.2
Sulfur (S), % 0 to 0.020
0
Titanium (Ti), % 0
0 to 0.1
Vanadium (V), % 0.15 to 0.25
0
Zinc (Zn), % 0
0 to 0.25
Residuals, % 0
0 to 0.15