Grade VDCrV Steel vs. EN 1.4621 Stainless Steel

Both grade VDCrV steel and EN 1.4621 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade VDCrV steel and the bottom bar is EN 1.4621 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 1730
500

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 410
970
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1410
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49
21
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
3.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
14
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.9
2.8
Embodied Energy, MJ/kg 26
41
Embodied Water, L/kg 49
140

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 61
18
Strength to Weight: Bending, points 41
18
Thermal Diffusivity, mm2/s 13
5.7
Thermal Shock Resistance, points 51
17

Alloy Composition

Carbon (C), % 0.62 to 0.72
0 to 0.030
Chromium (Cr), % 0.4 to 0.6
20 to 21.5
Copper (Cu), % 0 to 0.060
0.1 to 1.0
Iron (Fe), % 97.8 to 98.8
74.4 to 79.7
Manganese (Mn), % 0.5 to 0.9
0 to 1.0
Niobium (Nb), % 0
0.2 to 1.0
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.15 to 0.3
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.015
Vanadium (V), % 0.15 to 0.25
0