Grade VDSiCr Steel vs. EN 1.7711 Steel
Both grade VDSiCr steel and EN 1.7711 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is grade VDSiCr steel and the bottom bar is EN 1.7711 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 590 | |
210 to 280 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 80 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 1950 | |
690 to 930 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
250 |
Maximum Temperature: Mechanical, °C | 410 | |
430 |
Melting Completion (Liquidus), °C | 1440 | |
1460 |
Melting Onset (Solidus), °C | 1400 | |
1420 |
Specific Heat Capacity, J/kg-K | 480 | |
470 |
Thermal Conductivity, W/m-K | 46 | |
33 |
Thermal Expansion, µm/m-K | 13 | |
11 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
7.4 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
8.5 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.2 | |
3.0 |
Density, g/cm3 | 7.7 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.5 | |
2.3 |
Embodied Energy, MJ/kg | 20 | |
32 |
Embodied Water, L/kg | 48 | |
54 |
Common Calculations
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 25 | |
24 |
Strength to Weight: Axial, points | 70 | |
24 to 33 |
Strength to Weight: Bending, points | 45 | |
22 to 27 |
Thermal Diffusivity, mm2/s | 12 | |
8.9 |
Thermal Shock Resistance, points | 58 | |
24 to 32 |
Alloy Composition
Aluminum (Al), % | 0 | |
0 to 0.015 |
Carbon (C), % | 0.5 to 0.6 | |
0.36 to 0.44 |
Chromium (Cr), % | 0.5 to 0.8 | |
0.9 to 1.2 |
Copper (Cu), % | 0 to 0.060 | |
0 |
Iron (Fe), % | 96.6 to 97.8 | |
96 to 97.5 |
Manganese (Mn), % | 0.5 to 0.9 | |
0.45 to 0.85 |
Molybdenum (Mo), % | 0 | |
0.5 to 0.65 |
Phosphorus (P), % | 0 to 0.025 | |
0 to 0.025 |
Silicon (Si), % | 1.2 to 1.6 | |
0 to 0.4 |
Sulfur (S), % | 0 to 0.020 | |
0 to 0.030 |
Vanadium (V), % | 0 | |
0.25 to 0.35 |