Grade VDSiCrV Steel vs. Nickel 725
Grade VDSiCrV steel belongs to the iron alloys classification, while nickel 725 belongs to the nickel alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is grade VDSiCrV steel and the bottom bar is nickel 725.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
200 |
Poisson's Ratio | 0.29 | |
0.29 |
Reduction in Area, % | 48 | |
45 |
Shear Modulus, GPa | 80 | |
78 |
Tensile Strength: Ultimate (UTS), MPa | 2100 | |
860 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
320 |
Maximum Temperature: Mechanical, °C | 420 | |
980 |
Melting Completion (Liquidus), °C | 1440 | |
1340 |
Melting Onset (Solidus), °C | 1400 | |
1270 |
Specific Heat Capacity, J/kg-K | 480 | |
440 |
Thermal Expansion, µm/m-K | 13 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
1.5 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
1.6 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.3 | |
75 |
Density, g/cm3 | 7.7 | |
8.5 |
Embodied Carbon, kg CO2/kg material | 1.9 | |
13 |
Embodied Energy, MJ/kg | 26 | |
190 |
Embodied Water, L/kg | 50 | |
270 |
Common Calculations
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 25 | |
23 |
Strength to Weight: Axial, points | 75 | |
28 |
Strength to Weight: Bending, points | 47 | |
24 |
Thermal Shock Resistance, points | 63 | |
23 |
Alloy Composition
Aluminum (Al), % | 0 | |
0 to 0.35 |
Carbon (C), % | 0.5 to 0.7 | |
0 to 0.030 |
Chromium (Cr), % | 0.5 to 1.0 | |
19 to 22.5 |
Copper (Cu), % | 0 to 0.060 | |
0 |
Iron (Fe), % | 96.1 to 97.8 | |
2.3 to 15.3 |
Manganese (Mn), % | 0.4 to 0.9 | |
0 to 0.35 |
Molybdenum (Mo), % | 0 | |
7.0 to 9.5 |
Nickel (Ni), % | 0 | |
55 to 59 |
Niobium (Nb), % | 0 | |
2.8 to 4.0 |
Phosphorus (P), % | 0 to 0.020 | |
0 to 0.015 |
Silicon (Si), % | 1.2 to 1.7 | |
0 to 0.2 |
Sulfur (S), % | 0 to 0.020 | |
0 to 0.010 |
Titanium (Ti), % | 0 | |
1.0 to 1.7 |
Vanadium (V), % | 0.1 to 0.25 | |
0 |