Granite vs. Borosilicate Glass
Granite belongs to the natural stone classification, while borosilicate glass belongs to the glass and glass-ceramics. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is granite and the bottom bar is borosilicate glass.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 2200 | |
| 2000 |
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 67 to 80 |
| Flexural Strength, MPa | 24 | |
| 34 to 69 |
| Poisson's Ratio | 0.25 | |
| 0.21 |
| Tensile Strength: Ultimate (UTS), MPa | 39 | |
| 280 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 350 | |
| 360 |
| Specific Heat Capacity, J/kg-K | 840 | |
| 830 |
| Thermal Conductivity, W/m-K | 2.7 | |
| 1.2 |
| Thermal Expansion, µm/m-K | 7.4 | |
| 3.3 to 5.1 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 8.5 | |
| 5.0 to 34 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.9 | |
| 2.2 to 2.6 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 15 to 17 |
| Stiffness to Weight: Bending, points | 48 | |
| 55 to 61 |
| Strength to Weight: Axial, points | 3.8 | |
| 30 to 35 |
| Strength to Weight: Bending, points | 9.0 | |
| 36 to 43 |
| Thermal Diffusivity, mm2/s | 1.1 | |
| 0.54 to 0.63 |
| Thermal Shock Resistance, points | 5.4 | |
| 50 to 91 |