Grey Cast Iron vs. Grade G3000 Cast Iron
Both grey cast iron and grade G3000 cast iron are iron alloys. Their average alloy composition is basically identical. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is grey cast iron and the bottom bar is grade G3000 cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 300 | |
| 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 180 |
| Elongation at Break, % | 9.6 | |
| 9.6 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 69 | |
| 70 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 450 | |
| 220 |
| Tensile Strength: Yield (Proof), MPa | 98 to 290 | |
| 150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 270 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1390 |
| Melting Onset (Solidus), °C | 1180 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 490 |
| Thermal Conductivity, W/m-K | 46 | |
| 41 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.9 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 1.9 |
| Density, g/cm3 | 7.5 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.5 |
| Embodied Energy, MJ/kg | 21 | |
| 21 |
| Embodied Water, L/kg | 44 | |
| 44 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 37 | |
| 19 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 27 to 240 | |
| 65 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 5.8 to 17 | |
| 8.1 |
| Strength to Weight: Bending, points | 8.7 to 17 | |
| 11 |
| Thermal Diffusivity, mm2/s | 13 | |
| 11 |
| Thermal Shock Resistance, points | 6.0 to 17 | |
| 7.3 |
Alloy Composition
| Carbon (C), % | 3.1 to 3.4 | |
| 3.1 to 3.4 |
| Iron (Fe), % | 92.1 to 93.9 | |
| 93.1 to 94.4 |
| Manganese (Mn), % | 0.5 to 0.7 | |
| 0.6 to 0.9 |
| Phosphorus (P), % | 0 to 0.9 | |
| 0 to 0.15 |
| Silicon (Si), % | 2.5 to 2.8 | |
| 1.9 to 2.3 |
| Sulfur (S), % | 0 to 0.15 | |
| 0 to 0.15 |