Grey Cast Iron vs. S46500 Stainless Steel
Both grey cast iron and S46500 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grey cast iron and the bottom bar is S46500 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 190 |
| Elongation at Break, % | 9.6 | |
| 2.3 to 14 |
| Fatigue Strength, MPa | 69 to 170 | |
| 550 to 890 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 69 | |
| 75 |
| Shear Strength, MPa | 180 to 610 | |
| 730 to 1120 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 450 | |
| 1260 to 1930 |
| Tensile Strength: Yield (Proof), MPa | 98 to 290 | |
| 1120 to 1810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 280 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1450 |
| Melting Onset (Solidus), °C | 1180 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 470 |
| Thermal Expansion, µm/m-K | 11 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 15 |
| Density, g/cm3 | 7.5 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 3.6 |
| Embodied Energy, MJ/kg | 21 | |
| 51 |
| Embodied Water, L/kg | 44 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 37 | |
| 43 to 210 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 5.8 to 17 | |
| 44 to 68 |
| Strength to Weight: Bending, points | 8.7 to 17 | |
| 33 to 44 |
| Thermal Shock Resistance, points | 6.0 to 17 | |
| 44 to 67 |
Alloy Composition
| Carbon (C), % | 3.1 to 3.4 | |
| 0 to 0.020 |
| Chromium (Cr), % | 0 | |
| 11 to 12.5 |
| Iron (Fe), % | 92.1 to 93.9 | |
| 72.6 to 76.1 |
| Manganese (Mn), % | 0.5 to 0.7 | |
| 0 to 0.25 |
| Molybdenum (Mo), % | 0 | |
| 0.75 to 1.3 |
| Nickel (Ni), % | 0 | |
| 10.7 to 11.3 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.9 | |
| 0 to 0.015 |
| Silicon (Si), % | 2.5 to 2.8 | |
| 0 to 0.25 |
| Sulfur (S), % | 0 to 0.15 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 1.5 to 1.8 |