Hafnia vs. Alumina
Both hafnia and alumina are oxide-based engineering ceramics. There are 11 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is hafnia and the bottom bar is alumina.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 57 | |
| 220 to 370 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 2800 | |
| 650 to 1730 |
| Melting Onset (Solidus), °C | 2900 | |
| 2040 |
| Specific Heat Capacity, J/kg-K | 120 | |
| 870 to 940 |
| Thermal Conductivity, W/m-K | 1.1 | |
| 14 to 30 |
| Thermal Expansion, µm/m-K | 6.0 | |
| 6.7 to 8.2 |
Electrical Properties
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 9.0 | |
| 6.2 to 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.7 | |
| 3.4 to 4.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.3 | |
| 35 to 53 |
| Stiffness to Weight: Bending, points | 13 | |
| 57 to 62 |
| Thermal Diffusivity, mm2/s | 0.95 | |
| 3.7 to 10 |