Half-hard ASTM B780 Alloy vs. Half-hard ASTM F15

Half-hard ASTM B780 alloy belongs to the otherwise unclassified metals classification, while half-hard ASTM F15 belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is half-hard ASTM B780 alloy and the bottom bar is half-hard ASTM F15.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
190
Poisson's Ratio 0.36
0.3
Shear Modulus, GPa 30
73
Tensile Strength: Ultimate (UTS), MPa 440
680

Thermal Properties

Latent Heat of Fusion, J/g 140
270
Melting Completion (Liquidus), °C 860
1410
Specific Heat Capacity, J/kg-K 270
460
Thermal Expansion, µm/m-K 18
6.0

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 73
3.7
Electrical Conductivity: Equal Weight (Specific), % IACS 65
4.0

Otherwise Unclassified Properties

Density, g/cm3 10
8.3

Common Calculations

Stiffness to Weight: Axial, points 4.5
13
Stiffness to Weight: Bending, points 14
23
Strength to Weight: Axial, points 12
23
Strength to Weight: Bending, points 13
21
Thermal Shock Resistance, points 21
42

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Cadmium (Cd), % 0 to 0.050
0
Carbon (C), % 0
0 to 0.040
Chromium (Cr), % 0
0 to 0.2
Cobalt (Co), % 0
16 to 18
Copper (Cu), % 23.5 to 25.7
0 to 0.2
Iron (Fe), % 0 to 0.050
50.3 to 56
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0
0 to 0.1
Manganese (Mn), % 0
0 to 0.5
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 0.35 to 0.65
28 to 30
Silicon (Si), % 0
0 to 0.2
Silver (Ag), % 74 to 76
0
Titanium (Ti), % 0
0 to 0.1
Zinc (Zn), % 0 to 0.060
0
Zirconium (Zr), % 0
0 to 0.1