Hardened SAE-AISI D2 vs. Hardened SAE-AISI D5
Both hardened SAE-AISI D2 and hardened SAE-AISI D5 are iron alloys. Both are furnished in the hardened (H) condition. They have a very high 97% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is hardened SAE-AISI D2 and the bottom bar is hardened SAE-AISI D5.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 5.0 | |
| 5.4 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Rockwell C Hardness | 62 | |
| 63 |
| Shear Modulus, GPa | 75 | |
| 75 |
| Shear Strength, MPa | 1160 | |
| 1180 |
| Tensile Strength: Ultimate (UTS), MPa | 2000 | |
| 2030 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 270 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1430 |
| Melting Onset (Solidus), °C | 1390 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 31 | |
| 27 |
| Thermal Expansion, µm/m-K | 11 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.3 | |
| 4.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.1 | |
| 4.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.0 | |
| 13 |
| Density, g/cm3 | 7.7 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 3.5 |
| Embodied Energy, MJ/kg | 50 | |
| 51 |
| Embodied Water, L/kg | 100 | |
| 120 |
Common Calculations
| PREN (Pitting Resistance) | 15 | |
| 15 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 72 | |
| 73 |
| Strength to Weight: Bending, points | 46 | |
| 46 |
| Thermal Diffusivity, mm2/s | 8.3 | |
| 7.4 |
| Thermal Shock Resistance, points | 67 | |
| 67 |
Alloy Composition
| Carbon (C), % | 1.4 to 1.6 | |
| 1.4 to 1.6 |
| Chromium (Cr), % | 11 to 13 | |
| 11 to 13 |
| Cobalt (Co), % | 0 | |
| 2.5 to 3.5 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 81.3 to 86.9 | |
| 77.9 to 84.4 |
| Manganese (Mn), % | 0 to 0.6 | |
| 0 to 0.6 |
| Molybdenum (Mo), % | 0.7 to 1.2 | |
| 0.7 to 1.2 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 to 1.1 | |
| 0 to 1.0 |