Hexagonal Boron Nitride vs. Alumina-lime-silica Glass
Hexagonal boron nitride belongs to the non-oxide engineering ceramics classification, while alumina-lime-silica glass belongs to the glass and glass-ceramics. There are 10 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is hexagonal boron nitride and the bottom bar is alumina-lime-silica glass.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.9 to 2.1 | |
| 2.8 |
| Dielectric Strength (Breakdown Potential), kV/mm | 61 to 200 | |
| 34 |
| Elastic (Young's, Tensile) Modulus, GPa | 14 to 60 | |
| 90 |
| Electrical Dissipation At 1 Hz | 0.0017 | |
| 0.0022 |
| Electrical Dissipation At 1 MHz | 0.00075 to 0.0018 | |
| 0.0026 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 13 to 15 | |
| 12 |
| Flexural Strength, MPa | 18 to 140 | |
| 46 |
| Stiffness to Weight: Axial, points | 4.1 to 18 | |
| 18 |
| Stiffness to Weight: Bending, points | 42 to 69 | |
| 53 |
| Thermal Expansion, µm/m-K | 0.54 to 18 | |
| 4.3 |