Hexagonal Boron Nitride vs. Machinable Glass-ceramic
Hexagonal boron nitride belongs to the non-oxide engineering ceramics classification, while machinable glass-ceramic belongs to the glass and glass-ceramics. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is hexagonal boron nitride and the bottom bar is machinable glass-ceramic.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 21 to 250 | |
| 310 |
| Elastic (Young's, Tensile) Modulus, GPa | 14 to 60 | |
| 67 |
| Flexural Strength, MPa | 18 to 140 | |
| 96 |
| Poisson's Ratio | 0.11 | |
| 0.29 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1030 to 2350 | |
| 760 |
| Specific Heat Capacity, J/kg-K | 840 to 1610 | |
| 790 |
| Thermal Conductivity, W/m-K | 29 to 96 | |
| 1.2 |
| Thermal Expansion, µm/m-K | 0.54 to 18 | |
| 21 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 4.0 to 4.4 | |
| 6.4 |
| Dielectric Strength (Breakdown Potential), kV/mm | 61 to 200 | |
| 27 |
| Electrical Dissipation At 1 Hz | 0.0017 | |
| 0.0049 |
| Electrical Dissipation At 1 MHz | 0.00075 to 0.0018 | |
| 0.0050 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 13 to 15 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.9 to 2.1 | |
| 2.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.1 to 18 | |
| 14 |
| Stiffness to Weight: Bending, points | 42 to 69 | |
| 51 |
| Thermal Diffusivity, mm2/s | 9.9 to 34 | |
| 0.56 |