EN 1.3532 +S Steel vs. EN 1.3533 +S Steel
Both EN 1.3532 +S steel and EN 1.3533 +S steel are iron alloys. Both are furnished in the shearability treated condition. Their average alloy composition is basically identical.
For each property being compared, the top bar is EN 1.3532 +S steel and the bottom bar is EN 1.3533 +S steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 220 | |
| 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 750 | |
| 730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 440 | |
| 440 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 46 | |
| 47 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.9 | |
| 7.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.1 | |
| 9.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 5.0 | |
| 5.0 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 1.8 |
| Embodied Energy, MJ/kg | 25 | |
| 25 |
| Embodied Water, L/kg | 60 | |
| 60 |
Common Calculations
| PREN (Pitting Resistance) | 2.0 | |
| 2.1 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 26 | |
| 26 |
| Strength to Weight: Bending, points | 23 | |
| 23 |
| Thermal Diffusivity, mm2/s | 13 | |
| 13 |
| Thermal Shock Resistance, points | 22 | |
| 21 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 to 0.050 |
| Carbon (C), % | 0.14 to 0.18 | |
| 0.15 to 0.2 |
| Chromium (Cr), % | 1.0 to 1.4 | |
| 1.3 to 1.6 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.3 |
| Iron (Fe), % | 92.6 to 94.8 | |
| 92.9 to 94.9 |
| Manganese (Mn), % | 0.25 to 0.55 | |
| 0.4 to 0.7 |
| Molybdenum (Mo), % | 0.2 to 0.3 | |
| 0.15 to 0.25 |
| Nickel (Ni), % | 3.8 to 4.3 | |
| 3.3 to 3.8 |
| Oxygen (O), % | 0 to 0.0020 | |
| 0 to 0.0020 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |