Solder Alloy 102 vs. C14510 Copper

Solder alloy 102 belongs to the otherwise unclassified metals classification, while C14510 copper belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is solder alloy 102 and the bottom bar is C14510 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 38
120
Elongation at Break, % 48
9.1 to 9.6
Poisson's Ratio 0.39
0.34
Shear Modulus, GPa 14
43
Tensile Strength: Ultimate (UTS), MPa 31
300 to 320

Thermal Properties

Latent Heat of Fusion, J/g 46
210
Melting Completion (Liquidus), °C 180
1080
Melting Onset (Solidus), °C 180
1050
Specific Heat Capacity, J/kg-K 190
390
Thermal Conductivity, W/m-K 53
360
Thermal Expansion, µm/m-K 25
17

Otherwise Unclassified Properties

Density, g/cm3 8.8
8.9
Embodied Carbon, kg CO2/kg material 11
2.6
Embodied Energy, MJ/kg 180
42
Embodied Water, L/kg 930
310

Common Calculations

Stiffness to Weight: Axial, points 2.4
7.2
Stiffness to Weight: Bending, points 13
18
Strength to Weight: Axial, points 1.0
9.2 to 10
Strength to Weight: Bending, points 2.5
11 to 12
Thermal Diffusivity, mm2/s 32
100
Thermal Shock Resistance, points 2.4
11 to 12

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.050
0
Cadmium (Cd), % 0 to 0.0020
0
Copper (Cu), % 0 to 0.080
99.15 to 99.69
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0
Lead (Pb), % 36 to 37.5
0 to 0.050
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0
0.010 to 0.030
Silver (Ag), % 0 to 0.1
0
Tellurium (Te), % 0
0.3 to 0.7
Tin (Sn), % 62.5 to 63.5
0
Zinc (Zn), % 0 to 0.0010
0