Solder Alloy 111 vs. EN 1.0254 Steel

Solder alloy 111 belongs to the otherwise unclassified metals classification, while EN 1.0254 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is solder alloy 111 and the bottom bar is EN 1.0254 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 14
120
Elastic (Young's, Tensile) Modulus, GPa 33
190
Elongation at Break, % 35
27
Poisson's Ratio 0.4
0.29
Shear Modulus, GPa 12
73
Tensile Strength: Ultimate (UTS), MPa 41
430

Thermal Properties

Latent Heat of Fusion, J/g 41
250
Melting Completion (Liquidus), °C 220
1460
Melting Onset (Solidus), °C 180
1420
Specific Heat Capacity, J/kg-K 180
470
Thermal Conductivity, W/m-K 48
50
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 11
8.3

Otherwise Unclassified Properties

Density, g/cm3 9.3
7.9
Embodied Carbon, kg CO2/kg material 9.4
1.5
Embodied Energy, MJ/kg 160
19
Embodied Water, L/kg 830
47

Common Calculations

Stiffness to Weight: Axial, points 2.0
13
Stiffness to Weight: Bending, points 12
24
Strength to Weight: Axial, points 1.2
15
Strength to Weight: Bending, points 2.8
16
Thermal Diffusivity, mm2/s 29
13
Thermal Shock Resistance, points 3.5
14

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.2
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0 to 0.16
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 0 to 0.080
0 to 0.3
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
97.2 to 100
Lead (Pb), % 48.8 to 50.5
0
Manganese (Mn), % 0
0 to 1.2
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 0 to 0.010
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.35
Silver (Ag), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.020
Tin (Sn), % 49.5 to 50.5
0
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 0
0 to 0.020
Zinc (Zn), % 0 to 0.0010
0