Solder Alloy 113 vs. Grade CX2MW Nickel

Solder alloy 113 belongs to the otherwise unclassified metals classification, while grade CX2MW nickel belongs to the nickel alloys. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is solder alloy 113 and the bottom bar is grade CX2MW nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 32
220
Elongation at Break, % 32
34
Poisson's Ratio 0.4
0.29
Shear Modulus, GPa 11
84
Tensile Strength: Ultimate (UTS), MPa 39
620

Thermal Properties

Latent Heat of Fusion, J/g 40
330
Melting Completion (Liquidus), °C 230
1550
Melting Onset (Solidus), °C 180
1490
Specific Heat Capacity, J/kg-K 170
430
Thermal Conductivity, W/m-K 46
10
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 9.8
1.5

Otherwise Unclassified Properties

Density, g/cm3 9.5
8.9
Embodied Carbon, kg CO2/kg material 8.9
12
Embodied Energy, MJ/kg 150
170
Embodied Water, L/kg 800
290

Common Calculations

Stiffness to Weight: Axial, points 1.8
14
Stiffness to Weight: Bending, points 11
23
Strength to Weight: Axial, points 1.1
19
Strength to Weight: Bending, points 2.7
18
Thermal Diffusivity, mm2/s 28
2.7
Thermal Shock Resistance, points 3.4
17

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.5
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.25
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
20 to 22.5
Copper (Cu), % 0 to 0.080
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
2.0 to 6.0
Lead (Pb), % 53.4 to 55.5
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
12.5 to 14.5
Nickel (Ni), % 0 to 0.010
51.3 to 63
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.8
Silver (Ag), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.025
Tin (Sn), % 44.5 to 45.5
0
Tungsten (W), % 0
2.5 to 3.5
Vanadium (V), % 0
0 to 0.35
Zinc (Zn), % 0 to 0.0010
0