Solder Alloy 115 vs. N07041 Nickel
Solder alloy 115 belongs to the otherwise unclassified metals classification, while N07041 nickel belongs to the nickel alloys. There are 14 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is solder alloy 115 and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 28 | |
| 220 |
| Elongation at Break, % | 22 | |
| 14 |
| Tensile Strength: Ultimate (UTS), MPa | 36 | |
| 1400 |
Thermal Properties
| Melting Onset (Solidus), °C | 180 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 450 |
| Thermal Conductivity, W/m-K | 43 | |
| 11 |
| Thermal Expansion, µm/m-K | 27 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.9 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.6 | |
| 15 |
| Stiffness to Weight: Bending, points | 10 | |
| 25 |
| Strength to Weight: Axial, points | 1.0 | |
| 47 |
| Strength to Weight: Bending, points | 2.4 | |
| 34 |
| Thermal Diffusivity, mm2/s | 27 | |
| 3.0 |
| Thermal Shock Resistance, points | 3.4 | |
| 38 |