Solder Alloy 116 vs. R60901 Alloy
Both solder alloy 116 and R60901 alloy are otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is solder alloy 116 and the bottom bar is R60901 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 26 | |
| 98 |
| Elongation at Break, % | 18 | |
| 17 to 22 |
| Poisson's Ratio | 0.42 | |
| 0.34 |
| Shear Modulus, GPa | 9.3 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 34 | |
| 500 to 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 34 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 270 |
| Thermal Conductivity, W/m-K | 41 | |
| 17 |
| Thermal Expansion, µm/m-K | 27 | |
| 6.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 6.6 |
| Embodied Water, L/kg | 690 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.5 | |
| 8.3 |
| Stiffness to Weight: Bending, points | 9.8 | |
| 23 |
| Strength to Weight: Axial, points | 0.94 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 2.3 | |
| 21 to 24 |
| Thermal Diffusivity, mm2/s | 26 | |
| 9.7 |
| Thermal Shock Resistance, points | 3.4 | |
| 58 to 67 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.5 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.25 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 |
| Lead (Pb), % | 68.4 to 70.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 2.4 to 2.8 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 29.5 to 30.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 96.8 to 97.5 |
| Residuals, % | 0 | |
| 0 to 0.29 |