Solder Alloy 117 vs. Grade 15 Babbitt Metal
Both solder alloy 117 and grade 15 Babbitt Metal are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 81% of their average alloy composition in common. There are 16 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is solder alloy 117 and the bottom bar is grade 15 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 11 | |
| 21 |
| Elastic (Young's, Tensile) Modulus, GPa | 23 | |
| 23 |
| Poisson's Ratio | 0.42 | |
| 0.4 |
| Shear Modulus, GPa | 8.1 | |
| 8.2 |
Thermal Properties
| Latent Heat of Fusion, J/g | 31 | |
| 46 |
| Melting Completion (Liquidus), °C | 280 | |
| 280 |
| Melting Onset (Solidus), °C | 180 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 140 |
| Thermal Expansion, µm/m-K | 28 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 85 | |
| 17 |
| Density, g/cm3 | 11 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 6.1 | |
| 3.6 |
| Embodied Energy, MJ/kg | 100 | |
| 47 |
| Embodied Water, L/kg | 610 | |
| 840 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.2 | |
| 1.2 |
| Stiffness to Weight: Bending, points | 9.0 | |
| 9.0 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 to 0.5 | |
| 14.5 to 17.5 |
| Arsenic (As), % | 0 to 0.030 | |
| 0.8 to 1.4 |
| Bismuth (Bi), % | 0 to 0.25 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 to 0.050 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 to 0.6 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 0.1 |
| Lead (Pb), % | 78.4 to 80.5 | |
| 79 to 83.9 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 19.5 to 20.5 | |
| 0.8 to 1.2 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 to 0.0050 |